*CONCRETE COMPRESSION DAMAGE

Define compression damage properties for the concrete damaged plasticity model.

This option is used to define compression damage (or stiffness degradation) properties for the concrete damaged plasticity material model. The CONCRETE COMPRESSION DAMAGE option must be used in conjunction with the CONCRETE DAMAGED PLASTICITY, CONCRETE TENSION STIFFENING, and CONCRETE COMPRESSION HARDENING options. In addition, the option can be used with the CONCRETE TENSION DAMAGE option to specify tensile stiffness degradation damage and the CONCRETE FAILURE option to define material failure criteria.

This page discusses:

See Also
*CONCRETE DAMAGED PLASTICITY
*CONCRETE TENSION STIFFENING
*CONCRETE COMPRESSION HARDENING
*CONCRETE TENSION DAMAGE
*CONCRETE FAILURE
In Other Guides
Concrete Damaged Plasticity

ProductsAbaqus/StandardAbaqus/ExplicitAbaqus/CAE

TypeModel data

LevelModel

Abaqus/CAEProperty module

Optional parameters

DEPENDENCIES

Set this parameter equal to the number of field variable dependencies included in the definition of the compression damage, in addition to temperature. If this parameter is omitted, it is assumed that the compression damage behavior depends only on temperature. See Material Data Definition for more information.

TENSION RECOVERY

This parameter is used to define the stiffness recovery factor wt, which determines the amount of tension stiffness that is recovered as the loading changes from compression to tension. If wt=1, the material fully recovers the tensile stiffness; if wt=0, there is no stiffness recovery. Intermediate values of wt (0≤wt≤1) result in partial recovery of the tensile stiffness. The default value is 0.0.

Data lines to define compression damage

First line

  1. Compressive damage variable, dc.

  2. Inelastic (crushing) strain, ε~ci⁢n.

  3. Temperature.

  4. First field variable.

  5. Second field variable.

  6. Etc., up to five field variables.

The first point at each value of temperature must have a crushing strain of 0.0 and a compressive damage value of 0.0.

Subsequent lines (only needed if the DEPENDENCIES parameter has a value greater than five)

  1. Sixth field variable.

  2. Etc., up to eight field variables per line.

Repeat this set of data lines as often as necessary to define the dependence of the compressive damage behavior on crushing strain, temperature, and other predefined field variables.